M Gold
 

1. COLOR

Light to medium yellow back ground with or without wavy nature.

2. FINISHES 

Special inspection:

1. Watch for red colored aggregation.
2. Hair line cracks


 

Common inspection: 

1. Slabs would be evenly polished all over with out any scratches/patches.
2. Thickness as per tolerance (+/- 1 mm for slabs and +/- 0.5 mm for tiles)
3. Allowance would be given in measurement for peripheral defects.
4. Chipping or pitting and cracks not permitted within measured area.
5. Uneven polish, brick marks and scratches not allowed. Glosso metre 65/70+
6. Steps due to blade and other cutting defects not permitted.

3. AVAILABILITY

Can cater to any demand. At present we have 5 gang saws doing production for us. 

4. EXPORT COUNTRIES

All over the world.

5. DIFFERENT SIZES

1. Gang Saw size slabs: 2.6 m x 1.60 m and above
2. Vertical Size slabs: 1.8 m up (length) x 0.60 m - 1.20 m (width)
3. Tiles: 12”x12”x 10mm, 16”x16”x 10mm/12mm, 18”x18”x 12 mm, 24”x24”x20mm 
4. Cut to size: Any size can be fabricated as per customers’ requirement.


 

Technical Specification :
 
Compressive Strength 1366 Kg/cm2
Compressive Strength after Gelivity 1315 Kg/cm2
Ultimate Tensile Strength 120 Kg/cm2
Coeff. Thermal expansion 0.0066 mm/mco
Water Absorption 0.23 %
Impact Test-Min Fall Height 60 cm
Specific Gravity 2.595 Kg/m3
Hardness (Moh's Scale) 6.5
Chemical Composition :
 
Silica SiO2 67.07 %
Alumina Al2O3 16.51 %
Ferric Oxide Fe2O3 1.03 %
Ferrous Oxide FeO 4.12 %
Calcium Oxide CaO 1.35 %
Magnesium Oxide MgO 1.62 %
Sodium Oxide Na2O 2.63 %
Potassium Oxide K2O 4.75 %
Maganous Oxide MnO -
Titania TiO2 -
Phosphorous Pentoxide P2O5 -
Loss on Ignition   0.92 %